Description
LUPOY HI5007UT(Preliminary)
Injection Molding Grade, PA/ABS
High gloss, Heat Resistance, High Flow
Application: Automotive
Properites |
Test condition | Test Method | Unit |
Typical Value |
| Physical |
|
|
|
|
| Specific Gravity |
|
ISO 1183 |
kg/m³
|
1140 |
| Molding Shrinkage |
|
ISO 294-4 | % | 0.5-0.8 |
| Melt Flow Index |
250℃/2.16 260℃ / 5kg |
ISO 1133 |
g/10min
|
7.5 36 |
| Mechanical |
|
|
|
|
|
Tensile Strength
@ Yield
|
1mm/min 50mm/min |
ISO 527 |
Mpa | 60 |
|
Tensile Elongation
@ Break
|
50mm/min |
ISO 527 |
Mpa | 100 |
|
Flexural Strength Flexural Modulus |
2mm/min 2mm/min |
ISO 178 ISO 178 |
Mpa Mpa |
96 2,500 |
| Charpy Impact Strength |
23℃
-30℃
|
ISO 179 |
KJ/m²
KJ/m²
|
NB NB |
|
Charpy Impact Strength (Notched) |
23℃
-30℃
|
ISO 179 |
KJ/m²
KJ/m²
|
16 12 |
|
IZOD Impact Strength, 6.4mm (Notched) |
23℃
-30℃
|
ISO 180 |
KJ/m²
KJ/m²
|
45 |
| Thermal |
|
|
|
|
|
Heat Deflection Temperature 4.0mm
(Unannealed, Flatwise)
|
1.8Mpa 0.45Mpa |
ISO 75
|
℃
|
114 |
| Vicat Softening Temperature |
5daN, 50℃/h
|
ISO 306 |
℃ |
130 |
|
Flammability HB V-0 5VA 5VB |
|
UL94 |
Thickness mm mm mm mm |
1.5 |
Processing Guide (Injection Molding)
Front
Cylinder Temperature Middle
Rear
℃
℃
℃
240 ~ 270
240 ~ 275
240 ~ 275
Processing Parameters
Unit
Value
Drying Temperature
℃
80-100
Drying Time
hrs
4-6
Maximum Moisture Content
%
0.02
Melt Temperature
℃
250-275
Nozzle Temperature
℃
245~275
Mold Temperature
℃
50~70
Back Pressure
kg/cm2
10 ~ 40
Screw Speed
rpm
40~70